In this work, n-type Bi2Te2.7Se0.3 bulks are prepared by resistance pressure sintering technique from different particle sized powders, and the microstructure and electrical transport properties are investigated as function of the initial particle size distribution. With the initial particle size decreasing, more antisite defects, grain-boundaries and interface defects are introduced, and lead to a larger carrier concentration due to donor-like effect and a lower mobility due to the increasing grain boundary and carrier scattering, which results in a lower Seebeck coefficient and electrical resistivity. As a result, a maximum power factor of about 2.89mWmK(-2) at room temperature is achieved for the bulk sintered from the mix powders with different particle size distribution due to the optimization of the carrier concentration. The band gaps and the intrinsic excitation temperature are effectively adjusted by controlling the particle size in a narrow distribution. The sample sintered from the powders below 400mesh has the highest average power factor above 2.44mW mK(-2) in the whole testing temperature range due to the improving band gaps and intrinsic excitation temperature.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据