JOURNAL OF NATURAL FIBERS
卷 15, 期 1, 页码 21-28出版社
TAYLOR & FRANCIS INC
DOI: 10.1080/15440478.2017.1302387
关键词
conductive cotton; fabric characterization; fabric modification; in situ polymerization; laccase; pyrrole
资金
- Program for Changjiang Scholars and Innovative Research Team in University [IRT_15R26]
Conductive cotton fabric was prepared using laccase as catalytic agent, pyrrole as electric monomer and paratoluene sulfonic acid sodium salt as dopant. The electric resistance of the prepared conductive cotton fabric was 1.22 x 10(7) Omega compared to 3.11 x 10(11) Omega of the original cotton fabric. The abrasion test indicated that polypyrrole was well integrated with the cotton fibers. The conductive cotton fabric also had good antistatic performance and good UV shield capability at 280-400 nm compared to the original cotton fabric. Moreover, the coating of polypyrrole improved the thermo-decomposition behavior of cotton fabrics. Nevertheless, the prepared conductive cotton fabric preserved the same breaking strength as the original cotton fabrics. Compared with original cotton, conductive cotton showed lower gas permeability.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据