calcium sulfate; phosphogypsum; anhydrite; self-leveling mortars
类别
资金
- CNPq
- CAPES
An experimental study was conducted to investigate the potential use of phosphogypsum (PG) to produce self-leveling underlayments. The study was designed in two stages. Initially a phosphoanhydrite (PA) was produced by heating phosphogypsum at temperatures of 350 degrees C, 450 degrees C, 550 degrees C, and 650 degrees C. Two periods of heating were applied (2 and 4 h). The formation of anhydrite was determined by thermogravimetric analysis (DTA-TG) and confirmed by X-ray diffraction (XRD). The results show that anhydrite II was obtained at temperatures above 450 degrees C, and at higher calcination temperatures the PA solubility was lower. In the second stage of this research, the PA was used in self-leveling underlayments as the main binder in the ternary system comprised of calcium sulfate, calcium aluminate cement, and Portland cement. Self-leveling mortar screeds produced using PA (550 degrees C/4 h) and PA (650 degrees C/4 h) showed the best performance in terms of mechanical strength and no degradation was observed after immersion and immersion-drying tests. The formation of ettringite, identified by scanning electron microscopy (SEM), may have contributed to these results. Morphological changes were studied using the scanning electron microscopy (SEM) technique.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据