期刊
LUBRICANTS
卷 5, 期 3, 页码 -出版社
MDPI
DOI: 10.3390/lubricants5030032
关键词
tribology; surface engineering; laser surface texturing; mixed lubrication; size effects
资金
- Daimler AG
- Robert Bosch GmbH
- KSPG Automotive
- Kluber Lubrication Munchen KG
- German Research Foundation DFG [GR 4174/1]
Unidirectional sliding experiments with polished and laser textured steel surfaces were carried out to investigate the effects of different textured area densities, aspect ratios and dimple arrangements. The system was lubricated with Polyalphaolefin (PAO) at 100 degrees C and the contact pressure was 3 MPa. For measuring Stribeck curves, the sliding speed was controlled between 40 and 2000 mm/s. The textured area density was varied between 5% and 30%, with the lowest friction values found for 10%. Aspect ratios ranging from 0.02 to 0.2 were investigated and for 0.1 the lowest friction values were measured. The dimple arrangements tested were cubic, hexagonal and a random distribution for a textured area density of 10% and an aspect ratio of 0.1. Our results demonstrate that the dimple arrangement does affect friction values, hinting to the fact that individual texture elements do influence each other. The optimum dimple arrangement was found in a hexagonal packing. This systematic variation of these three key texturing parameters for the morphological texturing of a tribological surface with dimples will allow a strategic choice of texturing parameters. This makes the most of the tremendous potential that laser surface texturing has for reducing friction forces and thereby CO2 emissions.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据