CONSTRUCTION AND BUILDING MATERIALS
卷 152, 期 -, 页码 818-831出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.conbuildmat.2017.07.041
关键词
Mortar; Sugar cane bagasse ash (SCBA); Nanosilica; Mechanical properties; Durability; Absorption; RCMT; Electrical resistivity; Mercury intrusion porosimetry (MIP)
Influence of nanosilica and sugar cane bagasse ash (SCBA) on the mechanical and durability properties of mortar, is investigated in this study. Sixteen mortar mixtures were designed with a particular water to binder ratio of 0.485 and a sand to binder ratio of 2.75. Test specimens were prepared with 3% and 6% replacement of cement weight with nanosilica and a 10-30% replacement of cement weight with SCBA. A compressive strength test was applied to evaluate the mechanical performance of mortars containing nanosilica and SCBA. In addition, transport tests, chloride permeability, electrical resistivity and mercury intrusion porosimetry of single, binary, and ternary blended mortars were conducted to investigate the influence of replacement materials on durability properties of mortars. Nanosilica improved mechanical and durability properties of mortar, while SCBA did not have a substantial influence on mortar performance according to lower strength and durability at early ages. The addition of SCBA in mixtures containing nanosilica intensely decreased compressive strength at the ages of 3 days and 7 days. However, ternary mixture results showed the best performance in the long term. (C) 2017 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据