Hemp shiv; Hemp concrete; Aluminium sulfate; Calcium hydroxide; Compressive strength
资金
- Suranaree University of Technology
- Rajamangala University of Technology Isan (Nakhonratchasima)
- King Mongkut's University of technology Thonburi Thailand
- Thailand Research Fund (TRF)
- Khon Kaen University under TRF Senior Research Scholar contract - Thailand [RTA5780004]
This research presents the potential of hemp shiv for use as coarse aggregate in concrete. Hemp shiv was mineralized with aluminium sulfate Al-2(SO4)(3) and calcium hydroxide Ca(OH)(2) before being used as a coarse aggregate to produce hemp concrete. The cement to sand ratio was 1:2, the Al-2(SO4)(3) to Ca (OH)(2) ratio was 1:2, and the amount of superplasticizer was 1% by mass of cement. The compressive strength, density and water absorption of hemp concretes were tested. The results showed that at 28 days the compressive strength of hemp concrete was in the range of 15.0-17.0 MPa, density of 1420-1470 kg/m(3) and water absorption of 14.5-16.5%. The results indicated that the application of Al2(504)3 and Ca(OH)(2) for mineralization increased the compressive strength of hemp concrete by four times compared to that with non-mineralized hemp shiv. The use of Al-2(SO4)(3) improved the compressive strength of composites and the increase in the amount of Al-2(SO4)(3) also accelerated the setting and hardening of the matrix. (C) 2017 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据