Modified graphene oxide; Emulsifying property; Tribological property; Mechanism
资金
- EU Marie Curie CIG [PCIG10-GA-2011-303922]
- National Natural Science Foundation of China, China (NSFC) [21363008]
- Shanghai Municipal Science and Technology Innovation Action Plan Project [15540723600]
Graphene oxide (GO) was asymmetric chemically modified with myristyltrimethylammonium bromide (TTAB) to get modified graphene oxide (MGO). This MGO was used as an emulsifier and additive in oil-in-water emulsion. The emulsifying tests showed MGO greatly improved the stability of base emulsion and decreased its droplets size. Tribological test results showed that under the boundary lubrication condition with MGO-emulsion, the friction coefficient (COF) and the wear rate of the steel ball were decreased by about 18% and 48% respectively, comparing with base emulsion lubrication. The tribological mechanism of MGO-emulsion could be explained by the strong film-forming ability on the metal surface; the good lubricity of its small droplets; the formed adsorption film, transfer film and tribofilm between the contact surfaces.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据