TRIBOLOGY INTERNATIONAL
卷 109, 期 -, 页码 563-570出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.triboint.2017.01.031
关键词
Atmospheric plasma spraying; Elevated temperature; Heat treatment; Adhesive strength; Tribological properties
资金
- National Natural Science Foundation of China [51575505, 51471181, 51675508]
The NiAl-Mo-Ag and NiAI-CrO3-Mo-Ag composite coatings were fabricated by atmospheric plasma spraying with the substrate material of Inconel 718. The effect of heat treatment on the microstructure, adhesive strength, microhardness and tribological properties of NiAl-Cr2O3-Mo-Ag composite coating was investigated. The heat treatment temperatures were chosen as 400, 500 and 600 degrees C. The composition and microstructure of composite coatings were analyzed by X-ray diffraction (XRD), scanning election microscopy (SEM) and transmission electron microscopy (TEM). The results show that the addition of Cr2O3 could effectively reduce the wear rate of NiAl-Mo-Ag composite coating. The adhesive strength, microhardness and tribological properties of NiAI-Cr2O3-Mo-Ag composite coating were improved by heat treatment. After 500 degrees C heat treatment, the microstructure of composite coating became more homogeneous and the coating had the highest adhesive strength, microhardness and the best tribological properties. The sliding process could promote the silver, nickel and molybdenum occur tribo-chemical reaction to form silver molybdates and nickel molybdates lubricating films which were responsible for the good tribological properties of composite coatings at elevated temperatures.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据