DENTAL MATERIALS
卷 33, 期 11, 页码 1286-1297出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.dental.2017.07.019
关键词
Computer-aided design; Computer-aided manufacturing; Fatigue; Biaxial flexural strength; Piston-on-three ball; Roughness; Zirconia; Leucite glass ceramic; Lithium disilicate
资金
- CAPES/NUFFIC
Objectives. To assess the effect of machining on the flexural fatigue strength and on the surface roughness of different computer-aided design, computer-aided manufacturing (CAD/CAM) ceramics by comparing machined and polished after machining specimens. Methods. Disc-shaped specimens of yttria-stabilized polycrystalline tetragonal zirconia (Y-TZP), leucite-, and lithium disilicate-based glass ceramics were prepared by CAD/CAM machining, and divided into two groups: machining (M) and machining followed by polishing (MP). The surface roughness was measured and the flexural fatigue strength was evaluated by the step-test method (n = 20). The initial load and the load increment for each ceramic material were based on a monotonic test (n = 5). A maximum of 10,000 cycles was applied in each load step, at 1.4 Hz. Weibull probability statistics was used for the analysis of the flexural fatigue strength, and Mann-Whitney test (alpha = 5%) to compare roughness between the M and MP conditions. Results. Machining resulted in lower values of characteristic flexural fatigue strength than machining followed by polishing. The greatest reduction in flexural fatigue strength from MP to M was observed for Y-TZP (40%; M = 536.48 MPa; MP = 894.50 MPa), followed by lithium disilicate (33%; M = 187.71 MPa; MP = 278.93 MPa) and leucite (29%; M = 72.61 MPa; MP = 102.55 MPa). Significantly higher values of roughness (Ra) were observed for M compared to MP (leucite: M = 1.59 mu m and MP = 0.08 mu m; lithium disilicate: M = 1.84 mu m and MP = 0.13 mu m; Y-TZP: M = 1.79 mu m and MP = 0.18 mu m). Significance. Machining negatively affected the flexural fatigue strength of CAD/CAM ceramics, indicating that machining of partially or fully sintered ceramics is deleterious to fatigue strength. (C) 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据