THIN SOLID FILMS
卷 642, 期 -, 页码 311-315出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.tsf.2017.09.056
关键词
Electron irradiation; Proton irradiation; Degradation properties; Cu2ZnSnS4 solar cells; CZTS
类别
资金
- Inter-University Laboratory for Joint Use of National Institutes for Quantum and Radiological Science and Technology Facilities
- Photovoltaic Science and Technology Research Division under Research Institute for Science and Technology, Tokyo University of Science
The electrical and optical properties of electron or proton-irradiated Cu2ZnSnS4 (CZTS) solar cells were investigated. The normalized efficiency of CZTS solar cells decreased when fluence was greater than similar to 10 (15)cm(-2) for electron irradiation or 10(12)cm(-2) for proton irradiation. This tendency is quantitatively the same as that of Cu(In,Ga)Se-2 (CIGS) solar cells, and better than that of Si solar cells. One of the origins of degradation is the formation of deep defects such as Cu atoms substituted at Zn sites and nonradiative recombination centers in the CZTS layer, as suggested by the decreasing photoluminescence peak intensity at 1.2 eV with increasing irradiation fluence. On the other hand, the solar cell performance improved in the case of a small amount of electron or proton irradiation due to the bombardment soaking effect. These results indicate that the CZTS solar cells show excellent tolerance of electron and proton radiation, similar to a CIGS solar cell.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据