THIN SOLID FILMS
卷 644, 期 -, 页码 173-181出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.tsf.2017.09.051
关键词
Nanoindentation; Hard coating; Indenter radius effect; Substrate effect
类别
资金
- project M-ERA RUS+ LightMat4Space
- project Research Centre of Advanced Materials and Technologies for Recent and Future Applications PROMATECH, ITMS project [26220220186]
- [APVV-15-0168]
- [VEGA2/0187/15]
The FEM modelling combined with the experimental nanoindentation hardness and indentation modulus depth profiles with the indenter tips of different radii on hard W-C coating/softer steel substrate with different coating thicknesses, revealed the strong influence of the tip radius and coating thickness on the shape of hardness and indentation modulus depth profiles, and the subsequent underestimation of coating property values extracted from the profiles. The effects of tip radius and coating thickness on hardness profiles have the same physical reason - faster penetration of the zone of plasticity into substrate at the same relative indentation depths when the indenter tip radius increases and/or coating thickness is reduced. Thus, the validity of the 10% rule is limited also by the indenter radius. The main parameters critical for proper nanoindentation measurements in the studied W-C coating/steel substrate system include indenter tip radius <= 500 nm, coating thickness >= 0.5 mu m and the ratio of the tip radius to coating thickness <= 0.1.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据