SURFACE & COATINGS TECHNOLOGY
卷 328, 期 -, 页码 436-443出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2017.08.060
关键词
Ca-added flame resistant Mg alloy; Steam coating; Formation mechanism; Mg(OH)(2); Mg-Al layered double hydroxide
资金
- Japan Society for the Promotion of Science [16K18249]
- Japan Science and Technology Agency (JST), Adaptable and Seamless Technology Transfer Program through Target-driven RD (A-STEP) [AS2815047S]
- Grants-in-Aid for Scientific Research [16K18249] Funding Source: KAKEN
Corrosion resistant films were prepared on the Ca-added flame-resistant magnesium alloy AZCa612 by steam coating at different treatment time and temperature. The formation mechanism of the films was investigated by using the digital microscope, FE-SEM, XRD, FT-IR, XPS and the potentiodynamic polarization curve measurements in a 5 mass% NaCI aqueous solution. XRD, Fr-IR and XPS studies.indicated that the film was composed mainly of Mg(OH)(2) and carbonated-based Mg-Al LDHs. In addition, MgCO3 and AlO(OH) were also incorporated slightly in the film. The formation mechanism of the film on AZCa612 was proposed that amorphous Mg(OH)(2) was initially formed by reaction of steam and MgO as a natural oxide film on the substrate. With an increase in the temperature and pressure, the amorphous Mg(OH)(2) was crystallized, and further increase in temperature, pressure, and treatment time induced the formation of Mg-Al LDH and AlO(OH) in the film. (C) 2017 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据