期刊
CONSTRUCTION AND BUILDING MATERIALS
卷 157, 期 -, 页码 382-391出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.conbuildmat.2017.09.109
关键词
3D printing; Printability; Buildability; OPC-CSA blend; Heat of hydration
资金
- Hauts de France
- European Union
- European Regional Development Fund
Printing cementitious structures in 3D (3D Printing) requires the use of a mortar which setting is rigorously controlled. In this paper, a mix made out of two types of cement, ordinary Portland cement (OPC) and Calcium Sulfo-aluminate cement (CSA), was adopted to control the printability of a mortar. The latter was formulated in order to be extrudable, buildable and to reach a compressive strength comparable to that of a traditional mortar. Finally, a printable mix made out of 7% CSA and 93% OPC was developed. The cement paste of the developed mix was tested using isothermal calorimetry to study the impact of CSA on the heat of hydration of the mix. The mortar is first checked for the two characteristics of printability (extrudability and buildability) by a manual home-made device. Then, an estimation of the rheological properties of the mortar using a penetration test was done. Afterwards, the strength of the mortar was tested and a compressive strength of 88 MPa was found after 28 days for non-printed specimens and 79 MPa for printed specimens. (C) 2017 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据