期刊
ACTA CHIMICA SLOVENICA
卷 64, 期 3, 页码 644-653出版社
SLOVENSKO KEMIJSKO DRUSTVO
DOI: 10.17344/acsi.2017.3459
关键词
Surface modification; alumina nanoparticles; oleic acid; trimethoxyvinylsilane; dispersibility; lipophilic degree
资金
- Research Council of Shahrood University of Technology
The alumina nanoparticles (NPs) have been synthesized from reaction between alum with ammonia and then calcined the precipitate at 1200 degrees C for 4 h. Its surface was modified by oleic acid (OA) and trimethoxyvinylsilane (TMVS) in o-xylene at 50 degrees C. The alumina NPs and its modified were characterized by XRD, FT-IR, SEM, EDX and TGA. The TGA analysis indicated that the grafting amount of OA and TMVS were 10.5 and 8.0% respectively. The dispersion of modified NPs was determined in monomers such as methyl methacrylate (MMA), butyl acrylate (BuA) and styrene (St) and in solvents such as ethanol, hexane and acetone. The experimental results showed that the highest dispersion was happened NPs modified by oleic acid in n-hexane, while the highest dispersion was observed NPs modified by TMVS in acetone. The results indicate that NPs modified by oleic acid formed a stable dispersion in MMA and BuA. The highest amount of dispersion happened NPs modified by oleic acid in MMA and BuA in initial weight of 5 and 2.5% respectively, while stable dispersion is formed in styrene when TMVS is used as modifier. The highest amount of dispersion was happened NPs modified by TMVS in styrene in initial weight of 2.5%.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据