Graphene oxide; modified hummer's method; electrical characteristic; structure characateristic; functional group
资金
- Department of Higher Education, Ministry of Higher Education, Malaysia through Fundamental Research Grant Scheme (FRGS) [9003-00465]
The aim of this study is to study the influence of different solvents on the structure and electrical properties of graphene oxide. GO was obtained from graphite flakes by using modified hummers method in which different from conventional hummer's method. In this method, the experiment was synthesized without sodium nitrate (NaNO3) and ice bath, but carried out at room temperature. Prepared GO powders were then dissolved into different solvents, namely acetone and ethanol. Then spin-coated onto silicon wafer and IDE to produce acetone-GO (A-GO) and ethanol-GO (E-GO). SEM result shows that several square micron GO were obtained. In addition, due to the large agglomerates and contact between the flakes in E-GO sample, current-voltage pattern indicated the E-GO produced higher current flow than A-GO. Meanwhile, GO characterized using FTiR shows that both samples contain several functional groups such as hydroxyl, epoxy, carboxyl and carbonyl. Besides that, due to the lower diffraction peak of A-GO, XRD result shows the interlayer spacing of A-GO sample is slightly higher than E-GO sample. (C) 2017 The Authors. Published by Elsevier Ltd.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据