Fully polymeric and biobased CO2 sorbents composed of oxidized nanofibrillated cellulose (NFC) and a high molar mass polyethylenimine (PEI) have been prepared via a freeze-drying process. This resulted in NFC/PEI foams displaying a sheet structure with porosity above 97% and specific surface area in the range 2.7-8.3 m(2).g(-1). Systematic studies on the impact of both PEI content and relative humidity on the CO2 capture capacity of the amine functionalized sorbents have been conducted under atmospheric conditions (moist air with similar to 400 ppm of CO2). At 80% RH and an optimum PEI content of 44 wt %, a CO2 capacity of 2.22 mmol.g(-1), a stability over five cycles, and an exceptionally low adsorption half time of 10.6 min were achieved. In the 20-80% RH range studied, the increase in relative humidity increased CO2 capacity of NFC/PEI foams at the expense of a high H2O uptake in the range 3.8-28 mmol.g(-1).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据