RUSSIAN JOURNAL OF PHYSICAL CHEMISTRY A
卷 91, 期 10, 页码 1981-1986出版社
MAIK NAUKA/INTERPERIODICA/SPRINGER
DOI: 10.1134/S003602441710034X
关键词
polyacrylamide gel route; magnetic nanoparticle; SrFe12O19; magnetic properties
资金
- pre-research fund of the General Armament Department [9140A12030314HT05001]
A modified polyacrylamide gel route was used to prepare SrFe12O19 magnetic nanoparticles; ethylenediaminetetraacetic acid (EDTA) was used as a carboxyl chelating agent. The phase purity, morphology and magnetic properties of as-prepared samples were analyzed via X-ray diffraction (XRD), Raman spectroscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and vibrating sample magnetometery (VSM). XRD analysis indicates that high-purity SrFe12O19 magnetic nanoparticles can be synthesized at 700A degrees C in air. The characteristic peaks of as-prepared sample at 210, 283, 321, 340, 381, 411, 432, 475, 532, 618, 686, and 726 cm(-1) were observed in Raman spectra. SEM and TEM show that the synthesized SrFe12O19 magnetic nanoparticles are uniform with the mean particle size of 60 nm. VSM measurement shows that the maximum magnetic energy product (BH)(max) of sample prepared using EDTA as a chelating agent is higher than that of sample prepared using citric acid as a chelating agent.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据