期刊
ACS APPLIED MATERIALS & INTERFACES
卷 7, 期 44, 页码 24556-24565出版社
AMER CHEMICAL SOC
DOI: 10.1021/acsami.5b06170
关键词
dye-sensitized solar cells; nickel oxide; p-type; photocathode; artificial photosynthesis
资金
- Royal Society for a Dorothy Hodgkin Fellowship
- University of Nottingham
Mg Ni mixed metal oxide photocathodes have been prepared by a mixed NiCl2/MgCl2 sol-gel process. The MgO/NiO electrodes have been extensively characterized using physical and electrochemical methods. Dye-sensitized solar cells have been prepared from these films, and the higher concentrations of MgO improved the photovoltage of these devices; however, there was a notable drop in photo current with increasing Mg2+. Charge extraction and XPS experiments revealed that the cause of this was a positive shift in the energy of the valence band, which decreased the driving force for electron transfer from the NiO film to the dye and, therefore, the photocurrent. In addition, increasing concentrations of MgO increases the volume of pores between 0.500 and 0.050 mu m, while reducing pore volumes in the mesopore range (less than 0.050 mu m) and lowering BET surface area from approximately 41 down to 30 m(2) g(-1). A MgO concentration of 5% was found to strike a balance between the increased photovoltage and decreased photocurrent, possessing a BET surface area of 35 m(2) g(-1) and a large pore volume in both the meso- and macropore range, which lead to a higher overall power conversion efficiency than NiO alone.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据