Iron tailing powder; Hydration; Pore structure; Morphology; Strength
资金
- National Natural Science Foundation of China [51578039]
- China Postdoctoral Science Foundation [2015 M580992, 2016T90036]
- Open Fund of State Key Laboratory of High Performance Civil Engineering Materials [2015CEM010]
The early-age hydration characteristics of composite binder containing iron tailing powder were investigated by determining the hydration heat, non-evaporable water content, pore structure, and morphology of hardened paste as well as the compressive strength of mortar. The results show that the reaction degree of iron tailing powder is extremely low at early age. Addition of coarse iron tailing powder negatively affects the properties of composite binder paste and mortar. Compared to samples containing coarse iron tailing powder, the samples containing fine iron tailing powder show a large amount of hydration heat, high non-evaporable water content, fine pore structure of hardened paste and high compressive strength of mortar. The iron tailing powder significantly promotes the hydration of binder at low water-to-binder ratio. The iron tailing powder particles are well graded with cement particles in the paste, but the large iron tailing powder particles bond poorly with the surrounding hydrates. The decreasing ratio of compressive strength of mortar is much lower than the replacement level of iron tailing powder, especially for the mortar containing fine iron tailing powder at low water-to-binder ratio. (C) 2017 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据