Simultaneously improving the flame retardancy and mechanical properties for polyamide 6/aluminum diethylphosphinate composites by incorporating of 1,3,5-triglycidyl isocyanurate

The effect of 1,3,5-triglycidyl isocyanurate (TGIC) as a synergistic agent on the fire retardancy, thermal, and mechanical properties for polyamide 6/aluminium diethylphosphinate (PA6/AlPi) composites were investigated in detail by limiting oxygen index; vertical burning (UL-94); cone calorimeter; thermal gravimetric analysis; rheological measurements; and the tests of tensile, flexural, and Izod impact strength. The morphologies and chemical compositions of the char residue were investigated by scanning electron microscopy, X-ray photoelectron spectroscopy, and Fourier transform infrared spectra. The results demonstrated that AlPi and TGIC exerted an evident synergistic effect for flame retardant PA6 matrix, and the PA6/AlPi/TGIC composites with the thickness of 1.6mm successfully passed UL-94V-0 rating with the limiting oxygen index value of 30.8% when the total loading amount of AlPi/TGIC with the mass fraction of 97:3 was 11wt%. However, the samples failed to pass the UL-94 vertical burning tests when AlPi alone is used to flame retardant PA6 matrix with the same loading amount. The thermal gravimetric analysis data revealed that the introduction of TGIC promoted the char residue formation at high temperature. The rheological measurement demonstrated that the incorporation of TGIC improved the storage modulus, loss modulus, and complex viscosity of PA6/AlPi/TGIC composites comparing with that of neat PA6 and PA6/AlPi composites due to the coupling reaction between TGIC and the terminal groups of PA6 matrix. The morphological structures of char residues demonstrated that TGIC benefited to the formation of more homogenous and integrated char layer with no defects and holes on the surface comparing with that of PA6/AlPi composites during combustion. The higher melt viscosity of composites and the integrated and sealed char layer effectively inhibited the volatilization of flammable gas into the combustion zone and then led to the reduction of the heat release. The results of mechanical properties revealed that the incorporation of TGIC enhanced the mechanical properties for PA6/AlPi/TGIC composites comparing with that of PA6/AlPi composites with the same loading amount of flame retardant caused by the chain extension effect of TGIC. As a result, the flame retardancy and mechanical properties of PA6/AlPi composites simultaneously enhanced due to the introduction of TGIC.