A simplification of the overall method of producing trimethylsilylcellulose solutions in common organic volatile solvents is reported. Microcrystalline cellulose was derivatized aiming its solubilization in tetrahydrofuran and toluene to obtain ultra-thin films of cellulose by spin-coating. The main simplifi-cations are: 1) elimination of a swelling step before dissolution in the binary solvent N,N-dimethylacetamide/LiCl by using microcrystalline cellulose; 2) derivatization of cellulose OH groups with Si(CH3)(3) groups was successful with no additional catalyst, like trimethylsilyl chloride, the degree of substitution (DS) being 2.2 +/- 0.1. The DS at the extreme surface of the films was computed from the X-ray Photoelectron Spectroscopy data: using solely C is fitted component areas and, alternatively, from both C is and Si 2p areas. The DS estimated with a technique specific of the surface is close to the bulky one obtained from gravimetric measurements reported in the literature for materials synthesized with catalyst The topographic uniformity is shown by Atomic Force Microscopy. (C) 2017 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据