316N weldments; Pitting corrosion; Stress corrosion cracking; Delta ferrite
Pitting and stress corrosion cracking (SCC) studies on the 316N stainless steel (SS) weldments in as-welded (AW) and thermally aged (solution annealing (SA), 550 degrees C/4 h and 750 degrees C/1 h) conditions were carried out in acidic and acidic chloride media. Pitting corrosion and SCC resistance was the highest for SA weldment, which was attributed to homogenization of microstructural and microchemical heterogeneities during solution annealing. SA specimen showed the most stable passive film as compared to AW weldment because of higher amount of delta-ferrite in AW weld metal, which resulted in an increased heterogeneity and inferior SCC resistance in AW. Stability of passive film was found to be adversely affected due to heat treatments (at 550 degrees C/4 h and 750 degrees C/1 h) because of the precipitation of carbide and sigma phases. (C) 2018 Production and hosting by Elsevier B.V. on behalf of China Ordnance Society.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据