ENGINEERING FRACTURE MECHANICS
卷 134, 期 -, 页码 148-167出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.engfracmech.2014.12.005
关键词
Composites; Fracture mechanics; Mixed-mode fracture; Fractography; Aerospace vehicles
类别
资金
- Irish Research Council for Science, Engineering and Technology (IRCSET)
- Cytec Engineered Materials (CEM)
In the present study, the mixed-mode fracture toughness of three composite joint systems (2 secondary bonded and 1 co-cured) was investigated. The two secondary bonded systems predominantly resulted in cohesive failure with occasional interlaminar failure during mixed-mode loading while the co-cured system failed adhesively. This was attributed to moisture stored in the prepreg being released during the co-cure process. The mode II toughness was consistently 5-6 times that of the corresponding mode I case for each system. The increased toughness was due to a combination of an increased fracture surface area and a larger damage zone. (C) 2014 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据