The main target of this work was to investigate the thermal behavior and water resistance of geopolymer cement made from metakaolin as an aluminosilicate source using phosphoric acid solution (10M) as a hardener. The obtained geopolymer cements were cured at room temperature for 28days, the one part was treated at 200 degrees C, 400 degrees C, 600 degrees C, 800 degrees C and 1000 degrees C, and the others were soaked in water for 28days. The geopolymer cements were characterized by microstructural properties using X-ray diffractometry, infrared spectroscopy, microstructure, physical property based on water resistance and thermo-mechanical properties (thermal analysis, compressive strength). The results show that the compressive strength of the unheated geopolymer cement was 87.96MPa. The ones soaked in water revealed a strength of 40.71MPa. This indicates that the specimens soaked in water lose about 54% of their strengths. The X-ray patterns of heated geopolymer cements showed the formation of crystalline phases even at relatively low temperatures. It was typically found that the compressive strength of metakaolin-phosphate-based geopolymer cements decreases due to the hydrolysis of Si-O-P bonds in the presence of water.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据