期刊
ACS APPLIED MATERIALS & INTERFACES
卷 7, 期 19, 页码 10162-10168出版社
AMER CHEMICAL SOC
DOI: 10.1021/acsami.5b00218
关键词
sol-gel; sodium borosilicate glass; microstructure; Z-scan technique
资金
- Zhejiang Province Natural Science Foundation [LQ14E020006]
- National Nature Science Foundation of China [51272059, 51472183, 51172165]
The integrated and transparent sodium borosilicate glasses that contain copper exhibiting different colors, that is, red, green, and blue were synthesized by:combining the sol gel process and heat treatment in 1712 gas. To reveal substantially the cause of different colors in the glass, X-ray diffraction (XRD), transmission electron microscopy (TEM)and high resolution TEM (HRTEM) were systematically applied to investigate and determine the microstructure of the doped matter. The results showed three different crystals had for-led in the red, green and blue glass, and the sizes of these crystals were range from. 9 to 34, 1 to 6, and 1 to nm, respectively. The valence state of copper was further analyzed by X-ray photoelectron spectroscopy (XPS) and electron energy toss spectroscopy (EELS). The third-order nonlinear optical properties of the glasses were investigated by using Z-scan technique at the wavelength of 800 nm. Interestingly, the third-order nonlinear absorption of the red, green, and blue glass can be successfully controlled from reverse saturable absorption, no absorption to saturable absorption and the optical nonlinear susceptibility x(3) of the red, green and blue glass were estimated to be 6.4 X 10(-14), 1.6 X 10(-14), and 2.6 X 10-14 esu in the single-pulse energy of 0.36 mu J, respectively.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据