Lead-free solder; SAC305; SAC305-TiO2 composite solder; Microstructure; Nanocomposite; Mechanical properties
资金
- University of New South Wales (UNSW) [RG124326]
The present study explores the effect of nano-sized TiO2 ceramic particles on interfacial structure, creep and shear strength of eutectic Sn-3Ag-0.5Cu (SAC305 in wt.%) interconnect material under isothermal aging and thermal shock cycles. The study revealed that the non-reacting and non-coarsening TiO2 nanoparticles improved the creep, shear strength and thermal shock resistance through refined the structure. An interfacial microstructural analysis confirmed that a layer types Cu6Sn5 and Cu3Sn phases are grown at the interface of SAC305/Cu system. When SAC305 was in contact with the Au/Ni-plated Cu pad ball grid array (BGA) substrate, a ternary (Cu, Ni)-Sn phase was detected. The thickness of IMC phase is increased with the aging time. However, the growth of IMC layer as well as the IMC phases inside the matrix e.g., Ag3Sn, Cu6Sn5, and AuSn4 is slower in the composite interconnection systems than that of reference interconnection systems. Furthermore, during the thermal shock cycles some micro-cracks are found at the interface and matrix regions in the reference interconnection systems. The measured shear strength of composite interconnections exhibited higher values as compare to the reference interconnection systems. However, the thermal shock cycles degrades the shear strength of interconnection faster than the situation in isothermal aging.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据