LuAG:Ce ceramics; Lu3+ deficiency; Scintillation light yield; Non-stoichiometry; Antisite defects
资金
- China Scholarship Council (CSC)
- National Science Foundation of China [U1332202, 61475175, 51172262]
- Research Program and International Cooperation Program of Shanghai Sciences and Technology Commission Foundation [13JC1405800, 15520721000]
- Chinese Academy of Sciences Visiting Professor for Senior International Scientists [2013T2G0004, 2014VTB009]
- Czech Science Foundation [P204/12/0805]
Lu3-xAl5O12:Ce optical ceramics (Lu(3-x)AG:Ce, x = 1, 2, 3 and 4 at.%, respectively) with Lu3+ compositions ranging from 1 to 4 at.% below stoichiometry content were fabricated by solid state reaction method and further optimized by an air-annealing process. The effect of Lu3+ deficiency on the optical, luminescence and scintillation properties of such a non-stoichiometric Lu3-xAl5O12:Ce ceramics was investigated. Significant influence in the material densification was found leading to strong changes in the transparency, radioluminescence (RL) and scintillation response of these ceramics. Within the range of 1 4 at.% Lu3+ deficiency, Lu-Al antisite defects were suppressed effectively and the Lu(3-x)AG:Ce ceramics displayed an extremely high RL intensity which reaches similar to 4 times higher than that of the latest commercial LuAG:Ce single crystals while its transparency deteriorated. The microstructure, presence of foreign phases and charge traps acting in scintillation mechanism were also Characterized by means of SEM, back scattered electron imaging and thermoluminescence techniques, respectively. (C) 2016 Elsevier B.V. All rights reserved.