DOI: 10.1016/j.nimb.2017.02.004
关键词
Silicon carbide Schottky barrier diode; Deep level transient spectroscopy; Recrystallization; Swift heavy ion
类别
资金
- National Natural Science Foundation of China [61176096]
- Heavy Ion Research Facility in Lanzhou (HIRFL), China
In this paper, the phenomenon that the recrystallization effects of swift heavy Bi-209 ions irradiation can partially recovery damage with more than 1 x 10(10) ions/cm(2) is investigated by the degradation of the electrical characteristics of 4H-SiC Schottky barrier diode (SBD) with swift heavy ion irradiation. Deep level transient spectroscopy (DLTS) and Current-Voltage (I-V) measurements clearly indicated that E-0.62 defect induced by swift heavy ion irradiation, which was a recombination center, could result in the increase of reverse leakage current (I-R) at fluence less than 1 x 10(9) ions/cm(2) and the recovery of IR at fluence more than 1 x 10(10) ions/cm(2) in 4H-SiC SBD. The variation tendency of I-R is consisted with the change of E-0.62 defect. Furthermore, it is reasonable explanation that the damage or defect formed at low fluence in SiC may be recovered by further swift heavy ion irradiation with high fluence, which is due to the melting with the ion tracks of the amorphous zones through a thermal spike and subsequent epitaxial recrystallization initiated from the neighboring crystalline regions. (C) 2017 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据