Li-ion batteries; layered cathodes; Na2Mn3O7; capacity; insertion mechanism
资金
- Shell Technology Centre (STC) Bangalore
- Department of Science and Technology (DST, Govt. of India)
- Science and Engineering Research Board (SERB, Govt. of India) [PDF/2015/00217]
- SERB [ECR/2015/000525]
Exploring Mn-based battery insertion materials, layered Na2Mn3O7 was synthesized via single pot solid-state method. Rietveld analysis confirmed the formation of triclinic structured Na2Mn3O7 with P-1 symmetry. With no further optimization, the as-synthesized Na2Mn3O7 was found to be an efficient host for Li+ (de)intercalation. Na2Mn3O7 delivered a discharge capacity of similar to 160 mA h g(-1) by altering the redox couple Mn(IV)/Mn(III) with a nominal voltage of 3.12 V (vs Li/Li+). Interestingly, the first discharge of pristine Na2Mn3O7 led to the formation of LixNa2Mn3O7 (2 < x < 3) having completely different phase similar to the LiCoO2 structure. Lithiation triggered phase transformation from triclinic (P-1) to trigonal (R-3m) structure. This electrochemically reformed structure imparts stability to [Mn3O7](infinity)(-2) building layers, preventing irreversible capacity loss. Underlying a single-phase (solid-solution) redox mechanism, Na2Mn3O7 acts as a robust cathode material for Li-ion batteries.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据