期刊
THERMEC 2018: 10TH INTERNATIONAL CONFERENCE ON PROCESSING AND MANUFACTURING OF ADVANCED MATERIALS
卷 941, 期 -, 页码 1574-1578出版社
TRANS TECH PUBLICATIONS LTD
DOI: 10.4028/www.scientific.net/MSF.941.1574
关键词
Additive manufacturing; selective laser melting; fabrication condition; Inconel 718
Selective laser melting (SLM) process has advantages in building free shape and simplification of manufacturing process. Since Ni-base superalloys have lower ductility at lower temperature, it is difficult to produce the parts by means of other process like forging. Therefore, SLM process has already applied to produce Ni-base superalloy parts. However, SLM process needs a long process time comparing to casting and machining. One of the means to solve this problem is an application of the high scanning speed condition under high power laser output. In this research, the optimum fabrication condition of Inconel 718 superalloy by SLM process under high power and high scanning speed condition was investigated. As a result, the optimum fabrication condition was obtained using the process map. However, the relative density of the as-built specimen fabricated under high power and high scanning speed condition is lower than that of the as-built specimen fabricated under the condition of 300 W and 600 mm/s. This may be mainly due to the occurrence of gas-pores by key-hole like phenomenon in melt pool and the increase of spattering at high power and high scanning speed condition.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据