NANOSCALE
卷 9, 期 17, 页码 5641-5647出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c7nr00895c
关键词
-
类别
资金
- National Natural Science Foundation of China [61625401, 61574050, 11674072]
- Ministry of Science and Technology of China [2016YFA0200700]
- Strategic Priority Research Program of the Chinese Academy of Sciences [XDA09040201]
- CAS Key Laboratory of Nanosystem and Hierarchical Fabrication
- Youth Innovation Promotion Association CAS
Two-dimensional transition-metal dichalcogenides (TMDs) have attracted much research interest in the hydrogen evolution reaction (HER) due to their superior electrocatalytic properties. Beyond binary TMDs, ternary TMD alloys, as electrocatalysts, were also gradually acknowledged for their remarkable efficiency in HER. Herein, we successfully synthesized monolayer dendritic ternary WS2(1-x) Se-2x flakes possessing abundant active edge sites on a single crystalline SrTiO3 (STO(100)). And the obtained dendritic WS2(1-x) Se-2x flakes could be transferred intact to arbitrary substrates, for example, SiO2/Si and Au foils. Intriguingly, the transferred dendritic WS2(1-x) Se-2x flakes on Au foil demonstrate a significant HER performance, reflected by a rather lower Tafel slope of similar to 69 mV dec(-1) and a much higher exchange current density of similar to 50.1 mu A cm(-2) outshining other CVD-grown two-dimensional TMD flakes. Furthermore, our new material shows excellent stability in electro-catalyzing the HER, suggestive of its robustness for being an excellent electrocatalyst. We believe that this work broadens the outlook for the synthesis of two-dimensional TMDs toward satisfying the applications in electrocatalysis.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据