dihydrate phosphogypsum; dehydration temperature; setting time; compressive strength; plasticizers
类别
资金
- European Regional Development Fund within the Activity 1.1.1.2 Post-doctoral Research Aid of the Specific Aid Objective 1.1.1 To increase the research and innovative capacity of scientific institutions of Latvia [1.1.1.2/VIAA/1/16/050]
Dihydrate phosphogypsum (PG) from phosphate fertilizer production plant was considered as secondary raw material to produce gypsum binder. XRD was used to characterize mineral composition of raw material before and after heat treatment, as well as for hardened samples. Technological properties of obtained binder were determined regarding to the dehydration temperature between 100 degrees C and 180 degrees C and optimal heat treatment parameters for PG were found to obtain PG hemihydrate. Setting time of binder was tested by adding slacked lime additive or two different plasticizers (lignosulfonate and rosin resin based). Compressive strength and moisture content was determined for 2 h and 14 d old samples. Results indicate that higher heat treatment temperature of PG reduce time to decompose PG to hemihydrate and slightly increase the initial setting time of obtained binder. Addition of plasticizer reduced water-PG ratio from 0.80 to 0.43 and the setting time was increased with lignosulfonate based plasticizer. Early age (2 h) strength of binder was from 0.1 to 15 NfPa and after 14 d hardening it reached 2.5 to 29 MPa, giving a promising results considering PG as secondary raw material for binder production. (C) 2018 The Authors. Published by Elsevier Ltd.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据