期刊
ELECTROCHIMICA ACTA
卷 153, 期 -, 页码 448-455出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2014.11.173
关键词
Microporous carbon nanoparticles; Nitrogen-functionalization; Electrode; Supercapacitor; Ultrahigh-rate performance
资金
- National Natural Science Foundation of China [21207099, 21273162, 21473122]
- Science and Technology Commission of Shanghai Municipality, China [11nm0501000, 12ZR1451100]
- Large Equipment Test Foundation of Tongji University [2013063, 2013069]
Nitrogen-functionalized microporous carbon nanoparticles (N-MCNs) are prepared by direct carbonization of a novel polymer obtained from the Schiff base reaction of terephthalaldehyde and m-phenylenediamine. The carbonization temperature plays a crucial role in the porosity, surface chemistry and capacitive performance for the carbons. N-MCN850 sample shows a much larger specific surface area of 1938 m(2) g(-1), a higher specific capacitance of 397 F g(-1) and 145 F g(-1) at the current density of 0.1 and 100 A g(-1) in 6 M KOH aqueous electrolyte, respectively. The results indicate its outstanding capacitive behavior and ultrahigh-rate performance. In addition, the electrode shows excellent cycling stability along with 98% of the initial specific capacitance after 5000 charge/discharge cycles. (C) 2014 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据