Supercapacitor; Three-dimensional hierarchical ordered; porous carbon; Nano-array; Template
资金
- National Natural Science Foundation of China [51072173, 51272221, 51302239, 21203161]
- Specialized Research Fund for the Doctoral Program of Higher Education [20134301130001]
- Natural Science Foundation of Hunan Province, China [13JJ4051]
Three-dimensional hierarchical ordered porous carbons (3D HOPCs) have been successfully prepared through templating method using silica sphere nano-array as a hard template, triblock copolymer P123 as a soft template and sucrose as a carbon source, and used as the electrode materials for supercapacitors. The structure, morphology and physicochemical properties of the as-prepared 3D HOPCs are characterized by nitrogen adsorption-desorption isotherm, scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and cyclic voltammetry (CV), galvanostatic charge-discharge (GCD) tests, and cycle life measurements. The results show that the 3D HOPCs possess well-interconnected 3D hierarchical ordered porous structure. Especially, the 3D HOPC-80, of which the pore size is 4.01 nm, shows the specific surface area of 1182m2 g (1) and a specific capacitance of 247 F g (1) at the current density of 1 A g (1). Besides, the supercapacitors based on 3D HOPCs exhibit excellent rate performance, high energy densities of 7.5Wh kg (1) and 5.8Wh kg (1) at the power densities of 500Wkg (1) and 10000Wkg (1), respectively. Moreover, the supercapacitors using 3D HOPCs as electrode materials hold high capacitance retentions over 91% even after 10000 cycles. (C) 2014 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据