期刊
MICROPOROUS AND MESOPOROUS MATERIALS
卷 239, 期 -, 页码 195-208出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.micromeso.2016.10.008
关键词
Faujasite; Hierarchical; Template-free; Nanosheets; Catalysis
类别
资金
- U. S. Department of Energy [DE-FE0007632]
We report a facile synthesis method of hierarchical faujasitic structures from a sodium aluminosilicate composition. The critical experimental variable was the removal of water via heat from the aluminosilicate gel during the synthesis process. These gels were used as starting materials for synthesis. With these partially dehydrated gels, extensive zeolite nucleation did occur, and the extent was varied both with the degree of dehydration and the temperature at which the dehydrated sample was maintained. Nanoparticles of FAU and EMT were formed that pack together resulting in external surface areas of 249 -259 m(2)/g. In addition, under certain conditions of crystal growth, sheet like-structures arising from FAU-EMT intergrowths were observed. The interpenetration packing of the nanosheets lead to zeolitic particles with external surface areas in the range of 127-199 m(2)/g. The pore size distribution varied with sample preparation and ranged from 2 to 100 nm. These samples were characterized by N-2 adsorption, X-ray diffraction and electron microscopy. The thermal and hydrothermal stability was also studied. In order to evaluate the role of the higher external surface area on a chemical reaction, the dealkylation of 1,3,5-triisopropylbenzene was examined and the product distribution did reflect the mesoporous nature of the sample. (C) 2016 Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据