aluminum alloys; microstructure; x-ray phase analysis; heat treatment; hardness
资金
- Ministry of Education and Science of the Russian Federation [11.1760.2014/K]
- Government of the Russian Federation [218]
The structure and phase composition of addition alloys based on aluminum with Hf, Er, Gd, Yand Sm and the effect of low additions of these transition metals on the structure and properties of alloy Al - 0.2% Zr - 0.1% Sc are studied. It is shown that individual introduction of Y, Sm, Er, and Gd in an amount of 0.1% each causes formation of eutectic phases Al3Y, Al3Sm, Al3Er and Al3Gd, respectively. An indirect inference is that the additions of Y, Sm, Hf, Er and Gd raise the thermal stability of the Al-3 (Sc, Zr) dispersoids after annealing at 250A degrees C with a hold of up to 100 h; softening at 370A degrees C starts after holding for 54 h. Maximum hardening is detected in the case of 0.1% Er and attains 50 HV after a 54-h hold at 370A degrees C.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据