期刊
DALTON TRANSACTIONS
卷 48, 期 7, 页码 2491-2504出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c8dt04974b
关键词
-
资金
- National Natural Science Foundation of China [21371184, 21771028]
- National-Municipal Joint Engineering Laboratory for Chemical Process Intensification and Reaction
- Chongqing Key Laboratory of Chemical Process for Clean Energy and Resource Utilization
K-doped FeOOH/Fe3O4 nanoparticles with a size of 100 nm were grown on stainless steel (SS) hydrothermally. The effect of the synthetic conditions on compositions, morphologies and electrochemical performances was discussed, and the possible synthetic mechanism was proposed. The obtained K-doped FeOOH/Fe3O4/SS demonstrated a superior specific capacity of 396 mA h g(-1) (0.554 mA h cm(-2)) at 1 A g(-1) in 2 M KOH, which is the largest value reported so far. And it was also much larger than those of K-doped and -undoped FeOOH/SS samples. Furthermore the sample manifested an increasing capacity during the cycling test, which was probably associated with the doping of K+ as well as the coexistence of Fe(ii) and Fe(iii) in the structure. Based on density functional theory (DFT), the effect of the K-doping on the electron conductivity of the sample was theoretically investigated. In addition, a Co-Mo-O/Ni3S2/Ni foam (NF)//K-doped FeOOH/Fe3O4/SS asymmetric supercapacitor was fabricated, which can deliver a high energy density of 74.38 W h kg(-1) at a power density of 3.64 W kg(-1).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据