MATERIALS SCIENCE AND TECHNOLOGY
卷 33, 期 16, 页码 1964-1977出版社
TAYLOR & FRANCIS LTD
DOI: 10.1080/02670836.2017.1342018
关键词
Hot stamping; press hardening; boron steel; automotive lightweighting; automotive crashworthiness
资金
- Tata Steel Europe
- European Social Fund
Hot stamping was performed with seven novel boron steels, exhibiting various carbon contents and microalloy additions of Mo, V and Ni compared to the standard 22MnB5 boron steel. The lower carbon content of 15MnB5 resulted in total elongation in excess of 11.0%. The higher carbon content of 38MnB5 resulted in ultimate tensile strength in excess of 2000 MPa. The vanadium addition resulted in ultimate tensile strength in excess of 1600 MPa combined with total elongation in excess of 11.0%. The carbon and microalloy additions were concluded to give rise to improved mechanical properties in hot-stamped boron steel for automotive body engineering applications.