Evolution of microstructure and mechanical properties in a cold deformed nitrogen bearing TRIP-assisted duplex stainless steel after reversion annealing

出版社

ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2016.10.105

关键词

Duplex stainless steels; Deformation induced martensite; Reversion annealing mechanisms; Recovery; Recrystallization; Strain hardening behavior

向作者/读者索取更多资源

The effects of cold working and subsequent reversion annealing treatment were studied on the microstructural evolution and mechanical properties enhancement of a new cost effective nitrogen bearing duplex stainless steel (DSS). The cold rolling-reversion annealing cycles were carried out at various temperatures in the range of 1023-1373 K (750-1100 degrees C). The mechanical properties of processed materials were investigated by the tensile testing method at room temperature. A series of characterization methods including X-ray diffraction, ferritescope measurement, scanning electron microscopy and dilatometry examination were applied to phase analysis and interpreting the martensite to austenite reversion mechanisms. The results showed that the ferrite would recover and recrystallize prior to any austenite reversion transformation. The non-diffusional reaction was recognized as the predominant reversion mechanism in the entire range of annealing. The diffiisional transformation was also activated during isothermal annealing, but as the secondary reversion mechanism. The mechanical behavior evolution of specimens subjected to the partial, incomplete and complete reversion transformation showed that the specimen partially reversed at 650 degrees C/180 s reveals a low work hardening capability owing to diffusional reversed stable austenitic phase as well as the high fraction of alpha-martensite in the microstructure. In addition, comparing work hardening behavior of incomplete reversed specimen (annealed at 800 degrees C/180 s) and completely reversed fully recrystallized one (annealed at 1050 degrees C/180 s) indicated that the former possesses a higher potential to be strengthened by strain induced martensite formation than latter, due to the existence of less stable austenite phase. However, the work hardening capacity and plasticity of alloy continually increased by raising the annealing temperature.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据