期刊
出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2017.05.018
关键词
Nickel-base single crystal superalloy; Creep-fatigue interaction; Microstructure; Fracture morphology
类别
资金
- National Natural Science Foundation of China [51375387, 51210008]
Creep-fatigue interaction behavior of a single crystal nickel-base superalloy was studied at 980 degrees C and the microstructure was quantitatively analyzed. A three-stepped plate specimen had been designed to simultaneously observe microstructure changed under three different stresses. It was found that the distribution of gamma' size was basically consistent with lognormal probability scale under all three loading conditions. The average size of gamma' precipitates increased with the increasing of stress at the same interrupted time. Four different layers including oxide layer, gamma'-free layer, gamma'-reduced layer and gamma/gamma' layer can be observed on the cross-section of the specimens. The thickness of gamma'-free layer also increased with the increasing of stress. Numerous dimples and square-shaped facets were observed at the fracture surface and furthermore propagation of cracks from micropores to the boundary of the facets could be found, which showed the fracture behaviours of both creep and fatigue damage.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据