Shock wave compaction and sintering of mechanically alloyed CoCrFeMnNi high-entropy alloy powders

In this study, mechanically alloyed CoCrFeMnNi high-entropy alloy (HEA) powders were compacted using static and shock wave compaction methods followed by pressureless sintering. The microstructural evolution and the mechanical properties were analyzed using optical microscopy, scanning electron microscopy, finite element method simulations, and tensile tests. The alloy consists of an FCC phase with a minor amount of ZrO2 in the as milled and sintered condition. The presence of ZrO2 is due to the contamination during milling, and it led to the formation of composite microstructure after sintering. The static compaction of the alloyed powders resulted in an increase in compaction density (similar to 85 to 88%) with the increasing pressure (1-3 GPa), and the shock wave compaction of the alloyed powders resulted in the high relative density (similar to 95%) with relatively fine and isolated pores. After sintering, almost full densification (similar to 99.5%) with smaller grain size and better mechanical properties was achieved in the shock wave compacted specimens as compared to the sintering of static compacted specimens. The sintered shock wave compacted specimen exhibited high yield strength of similar to 630 MPa and uniform strain distributions.