Precipitation hardenable WE43 magnesium alloy containing yttrium and rare earth elements was processed by ECAP. Microstructure, phase composition, mechanical properties and texture of the processed material was investigated by several complementary techniques. Substantial precipitation during ECAP led to exceptional grain refinement with the resulting average grain size of similar to 340 nm. The processed material exhibited previously unreported weak texture without a typical component usually observed in magnesium alloys processed similarly. The observed texture resulted from a massive particle-induced recrystallization during the processing through ECAP. The ultra-fine grain microstructure, the high density of Mg5RE particles and the specific texture resulted in the significant strengthening of the ECAPed material. The yield compression strength of similar to 427 MPa was by 340% higher than that of the initial as-cast condition and by 210% higher than that of the peak age-hardened one.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据