期刊
出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2017.08.048
关键词
Titanium alloy; Discontinuous yielding; Hot deformation; Phase transformation; Microstructure
类别
资金
- China Friction Stir Welding Center
- Beijing Friction Stir Welding Technology Limited Company [20140010]
Discontinuous yielding behavior of TC11 alloy was found during hot compression tests at temperatures of 1000-1050 degrees C and the strain rate of 10 s(-1). The flow stress showed a rapid drop and subsequent oscillation after peak stress before true strain of 0.15. It was proved to be the result of the stress induced phase transformation (alpha ->beta), which introduced softening effect for the generation of new beta phase. Moreover, the magnitude of the stress drop increased with the increasing of the fraction of stress induced phase transformation. In addition, these newly generated beta phase were further deformed by subsequent compression strain. As a result, the phase transformation of beta ->alpha '' was found in final quenched microstructures.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据