Hydrogen embrittlement; Solution-treated temperature; Prior austenite grain size; Precipitation
类别
资金
- Doctoral Research Assistant Foundation of Xi'an Jiaotong University
The effect of solution-treated temperature on hydrogen embrittlement of 17-4 PH stainless steel is investigated. Electrochemical hydrogen charging and slow strain rate tensile tests were used to calculate the index of susceptibility to hydrogen embrittlement. Fracture morphology and microstructure of the steel were observed by scanning electron microscope, optical microscope and transmission electron microscope. The results show that as the solution-treated temperature increases from 890 degrees C to 1090 degrees C, the susceptibility to hydrogen embrittlement of the steel firstly decreases and then increases, Based on the experimental results, it is deemed that the susceptibility to hydrogen embrittlement is determined by the result of a combined effect of the prior austenite grain size and copper precipitation. In addition, hydrogen permeation test result reveals that hydrogen-induced cracking of 17-4 PH steel is closely related to the diffusion behavior of hydrogen in alloys.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据