A novel white light emitting phosphor KCaBi(PO4)(2):Dy3+ for UV excitations has been synthesized by the solid state reaction technique. The powder X-ray diffraction patterns, Rietveld refinement and XPS were utilized to confirm the phase composite and crystal structure. The excitation and emission spectra, decay curves and chromaticity coordinates of the as-prepared phosphors were characterized to investigate the photoluminescence properties for application in white light-emitting diodes. The results revealed that the KCaBi(PO4)(2):Dy3+ phosphors can be effectively assimilated with near ultraviolet, and exhibit two emission bands peaked at 480 nm(blue light) and 580 nm(yellow light) originating from the F-4(9/2)-H-6(15/2), F-4(9/2)-H-6(13/2) transitions of Dy3+, respectively. The critical distance was calculated to be about 17.96 angstrom and the concentration quenching mechanism was verified as dipole-dipole interaction. Additional, the optimal chromaticity coordinates were determined to be (0.3118, 0.3309) and a better thermal stability of the phosphors have been illustrated. (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据