期刊
INTERNATIONAL JOURNAL OF AUTOMATION TECHNOLOGY
卷 13, 期 3, 页码 330-337出版社
FUJI TECHNOLOGY PRESS LTD
DOI: 10.20965/ijat.2019.p0330
关键词
additive manufacturing; powder bed fusion; pore; temperature
The powder bed fusion (PBF) technique is a metalbased additive manufacturing (AM) method in which metal powder is deposited on a substrate and melted by selective laser-beam irradiation. Given that the process and parameters of metal-based AM are complicated, there are various problems in high-precision fabrication. One of these is that although metalbased AM can be used for fabrication of high-density parts, pores can easily form inside the fabricated structure owing to process instabilities. Pore formation degrades the mechanical strength of the fabricated structure. Therefore, this study investigated the pore formation mechanism inside a structure fabricated by PBF. Pore suppression by controlling the substrate temperature was also evaluated. Smalland large-sized pores with diameters of 10 mu m and more than 50 mu m, respectively, were found. Furthermore, differences in pore formation in the crosssection of the fabricated structure were observed owing to a variation in the volume-specific energy density and substrate temperature. At a substrate temperature of 25 degrees C, the number of pores decreased more at the upper position than at the lower position owing to repeated melting and solidification under the laser-beam irradiation. At a substrate temperature of 200 degrees C, the number of pores decreased significantly more than at 25 degrees C. Furthermore, as the substrate temperature increased, the wettability of the molten metal improved, resulting in smaller contact angles of the fabricated structure in the single-line track. In PBF, multiple lines are fabricated in each layer. At low substrate temperatures, interstices were formed between the lines owing to the low wettability of the molten metal. These interstices acted as the origins of pores when the next layer was fabricated. Heating the substrate made the surface of the structure smooth owing to the high wettability of the molten metal and a reduction in the number of pores. Therefore, the formation of large pores could be reduced by controlling the substrate temperature.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据