期刊
JOURNAL OF THE CERAMIC SOCIETY OF JAPAN
卷 127, 期 7, 页码 474-477出版社
CERAMIC SOC JAPAN-NIPPON SERAMIKKUSU KYOKAI
DOI: 10.2109/jcersj2.19048
关键词
epsilon-Fe2O3; kappa-Al2O3; GaFeO3; Ferroelectric; Ferrimagnetism; Multiferroic
资金
- JSPS KAKENHI [15H02292, 19H02426, 17H06240, 18K19126, 16H06794, 18K14122]
- MEXT Elements Strategy Initiative to form Core Research Center, Collaborative Research Project of Laboratory for Materials and Structures, Institute of Innovative Research (Tokyo Institute of Technology)
- Hattori Hokokai Foundation
- Murata Science Foundation
- Grants-in-Aid for Scientific Research [17H06240, 15H02292, 18K14122, 16H06794] Funding Source: KAKEN
RhxFe2-xO3 solid-solution epitaxial thin films were prepared by pulsed laser deposition. The ferroelectricity of Rh0.15Fe1.85O3 thin film was presented by the result of piezoelectric force microscopy phase and amplitude loops measured at room temperature. Ferrimagnetism at room temperature is confirmed by the magnetic hysteresis loop. The coercive field of Rh0.15Fe1.85O3 thin film at 5K is 12 kOe, which is larger than that of epsilon-Fe2O3. Rh0.15Fe1.85O3 is confirmed to be a room temperature multiferroic material. (C) 2019 The Ceramic Society of Japan. All rights reserved.