In this study, we fabricated a bulk-heterojunction organic photodetector with high detectivity by using a naphtho[1,2-c:5,6-c]bis[1,2,5]thiadiazole-based narrow-bandgap -conjugated polymer of PNTT as the donor and a fullerene derivative PC71BM as the acceptor. The relatively high mobility of PNTT allows the construction of a thick-film photoactive layer, which results in an increase in external quantum efficiency and a dramatic reduction in the dark current density. The combination of these advantages leads to an obvious increase in the detectivity and enhanced film thickness. A device based on a film thickness of 400 nm exhibited a very low dark current density of 0.33 nA cm(-2) and rectification in the order of 10(5) in the range of +/- 2 V. The resulting device exhibited high detectivity exceeding 10(13) cm Hz(1/2) W-1 in the range of 350 to 800 nm, with a maximum detectivity of 4.00 x 10(13) cm Hz(1/2) W-1 and a responsivity of 0.4 A W-1 at a working wavelength of 760 nm under a reverse bias of -0.1 V, which is among the highest values reported so far for organic photodetectors at this working wavelength without extra gains.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据