Failure analysis of a field brittle fracture composite insulator: characterisation by X-ray photoelectron spectroscopy analysis

期刊

HIGH VOLTAGE
卷 4, 期 2, 页码 89-96

出版社

INST ENGINEERING TECHNOLOGY-IET
DOI: 10.1049/hve.2018.5084

关键词

resins; failure (mechanical); X-ray photoelectron spectra; composite insulators; fractography; brittle fracture; glass fibre reinforced plastics; surface morphology; oxidation; X-ray photoelectron spectroscopy analysis; field brittle fracture composite insulator; fracture surface; glass-fibre-reinforced polymer rod; failure analysis; classical brittle fracture morphology; macroscopic fractography; microscopic fractography; oxidation; silicate glass network; epoxy resin matrix; leaching; brittle fracture

向作者/读者索取更多资源

In the present work, a field brittle fracture composite insulator was collected and examined with the purpose of obtaining a better understanding of the failure features. Firstly, the macroscopic and microscopic fractography of this fractured composite insulator was observed confirming that the classical brittle fracture morphology features appeared in this field failed composite insulator. Secondly, the X-ray photoelectron spectroscopy (XPS) analysis was performed on the fracture surface of the glass-fibre-reinforced polymer rod. By examining the XPS survey spectra and high-resolution XPS spectra for nitrogen, sulphur, silicon, calcium, aluminium, boron and carbon elements, the type of the glass fibre and the acid source responsible for this brittle fracture composite insulator were confirmed. Furthermore, the oxidation of the silicate network of glass fibre at the fracture surface was first observed, meanwhile, the oxidation of the epoxy resin matrix was also observed. The leaching of non-silicate constituents leading to a high-silica glass fibre was also observed; moreover, in comparison with the calcium and aluminium elements, the boron element resides in the silicate network was more preferential to be leached. The present work provides an insight into the brittle fracture in high voltage composite insulator from chemical properties point of view.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.6
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据