Rare-earth phosphates; Thermal barrier coatings (TBCs); Calcium-magnesium-alumina-silicate (CMAS); Apatite
资金
- National Natural Science Foundation of China [51501127, 51375332]
- Natural Science Foundation of Tianjin [16JCQNJC02900]
Calcium-magnesium-alumina-silicate (CMAS) attack has been considered as a significant failure mechanism for thermal barrier coatings (TBCs). As a promising series of TBC candidates, rare-earth phosphates have attracted increasing attention. This work evaluated the resistance characteristics of LnPO(4) (Ln = Nd, Sm, Gd) compounds to CMAS attack at 1250 degrees C. Due to the chemical reaction between molten CMAS and LnPO(4), a dense, crack-free reaction layer, mainly composed of Ca(3)Ln(7)(PO4)(SiO4)(5)O-2 apatite, CaAl2Si2O8 and MgAl2O4, was formed on the surface of compounds, which had positive effect on suppressing CMAS infiltration. The depth of CMAS penetration in LnPO(4) (Ln = Nd, Sm, Gd) decreased in the sequence of NdPO4, SmPO4 and GdPO4. GdPO4 had the best resistance characteristics to CMAS attack among the three compounds. The related mechanism was discussed based on the formation ability of apatite phase caused by the reaction between molten CMAS and LnPO(4). (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据